What is the magnitude of the maximum stress that exists at the tip of an internal crackhaving a radius of curvature of 1.9 x 10" mm and a crack length of 3.8 x 10 mm when atensile stress of 140 MPa is applied?4.5. A ceramic matrix composite contains internal flaws as large as 0.001 cm in length. Theplane strain fracture toughness of the composite is 45 and the tensile strength is 550 MPa.Will the flaw cause the composite to fail before the tensile strength is reached? Assumethat Y 1A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is to be subjected to atensile load. If the rod is to experience neither plastic deformation nor an elongation ofmore than 1.3 mm. when the applied load is 29,000 N, which of the four met ls or alloyslisted below are possible cardidates? Justify your choice(s).Materia!ModulusofYieldTensiieStrength(MPa)Elasticity(GPa)Strength(MPa)Aluminium alloy70255420Brass alloy100345420Сopper110210

4. Given Normal stress = 140 MPa Crack length, a = 3.8 x 10-2 mm Radius of…

Answered: What is the magnitude of the having a…

Engineering

Mechanical Engineering

What is the magnitude of the having a radius of curvature o tensile stress of 140 MPa is ar 4.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A structural beam is built from steel with a yield strength of 345 MPa. The structure has a minimum service temperature of 5 oC, where the fracture toughness of the steel KIC = 60 MPam. What is the minimum surface crack lengths that must be detected by quality control to ensure that the full yield strength of the steel is available in the beam? Assume geometric parameter Y = 1 and plain strain conditions. Answer in millimeters.
1.) Assume that a wing component on an airplane is made of an aluminum alloy with a plane strain fracture toughness of It was found that when the maximum internal crack length is 2.5 mm, breakage occurs at a load of 365 MPa. Find the stress level at which a critical internal crack length of 5.0 mm will fracture for the identical component and alloy. 2.) An S-five ninety alloy specimen nine hundred mm long will be subjected to eighty MPa tensile stress at eight hundred and fifteen degrees celcius. Later after five thousand of hours, compute its elongation. Consider a sum of one point five mm in the both immediate and main creep elongations. - Please answer this 2 and indicate the givens. Thank you
Question 2 A machine component is made of Aluminium alloy having an ultimate tensile stress Ou = 350MPa, a fracture toughness Kic= 40 MPa√m and a geometry factor Y=1.12. The component is subject to cyclic tensile stress of 200 MPa and cyclic compressive stress of 70 MPa. Before the operation, using an ultrasonic non-destructive testing technique, it was found that there is an edge crack of length 2mm. The crack growth C(AK)m, where is in m/cycle, AK ΔσΥ νπα , C ~ 2.2×10-12 da rate is given by da dN dN and m=3.2. Find the critical crack length. = =
A ceramic part for a jet engine has a yield strength of 75,000 psi and a plane strain fracture toughness of 5,000 psiVin. To be sure that the part does not fail, we plan to ensure that the maximum applied stress is only one-third of the yield strength. We use a nondestructive test that will detect any internal faws greater than 0.05 in. long. Assuming that f = 1.4, does our nondestructive test have the required sensitivity? Explain. A manufacturine proorssthat unintention
Question 6 What is the calculated fracture toughness, K, for the perspex specimen in MPa root m? Give your answer to 2 decimal places. P = 250 N, crack length = 5.5 mm W= 13.3 mm, B = 5.45 mm Note that the span length (s) is 38mm. Take f(a/W) as 0.78
An Al2O3 part contains both internal cracks with a maximum length of 0.075 mm, and external cracks with a maximum length of 0.05 mm. At what applied stress will the internal cracks begin to propagate? At what applied stress will the external cracks begin to propagate? The fracture toughness KIC = 1.76 MPa x m1/2, Y=1.
In designing a ceramic part for a jet engine, to ensure that the part does not fail, we plan to ensure that the maximum applied stress is only one-third of the yield strength. The yield strength of this CMC part for a jet engine is 520 MPa, and its plane strain fracture toughness is 5.5 MPa√?. We utilize a nondestructive test to find any internal faults that are longer than 1.27 mm. Does our non-destructive test have the requisite sensitivity if Y = 1.4? Explain.
A Copper specimen of circular cross-section is subjected to a tensile test. The data obtained are: Length of Specimen = 329 mm; Diameter of Specimen = 39 mm; Load at Yield Point = 130 kN; Maximum Load = 219 kN; Load at fracture = 118kN Determine the following: 1) Find initial area of the test specimen 2) Yield Stress 3) Ultimate Stress 4) Fracture stress 5) Find the strain for 0.058mm elongation.
Question: Some aircraft component is fabricated from an aluminum alloy that has a plane strain fracture toughness of 40 MPa sqrt(m) (36.4 ksi sqrt(in.)). It has been determined that fracture results at a stress of 300 MPa (43,500 psi) when the maximum (or critical) internal crack length is 4.0 mm (0.16 in.). For this same component and alloy, will fracture occur at a stress level of 260 MPa (38,000 psi) when the maximum internal crack length is 6.0 mm (0.24 in.)? Why or why not?
During stress-strain test, the unit deformation at a stress of 35 MPa was observed to be 167 x 10^-6 m/m and at a stress of 140 MPa it was 667 x 10^-6. If the proportional limit was 200 MPa, what is the modulus of Elasticity (GPa)? What is the strain corresponding to a stress of 80 MPa?
6. A ceramic part for a jet engine has a yield strength of 648 MPa and a plane strain fracture toughness of 8.49 MPam 4. To be sure that the part does not fail, we plan to ensure that the maximum applied stress is only one-third of the yield strength. We use a nondestructive test that will detect any internal flaws greater than 0.27 mm long. Assuming that the Y constant is 1.4, does our nondestructive test have the required sensitivity? Explain.
A specimen of a steel alloy with a plane strain fracture toughness of 22.1 MPavm. The largest surface crack is 0.6 mm long? Assume that the parameter Y has a value of 0.5. What is the critical stress in MPa. Write your answer with 2 decimal places. Answer: 0 dºvo vo (0) 00 00, GM