Question
Chapter 2, Problem 2.89P
To determine
The final height of the specimen.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
One spring is placed inside the other, not touching each other, and compressed between a pair of parallel plates until the distance between the plates is 40 mm. Make a neat detailed sketch of the spring and plate assembly. If G = 83 GPa for both springs, calculate the following:
1. The force applied to the spring assembly.
2. The shear stress induced in each spring.
3. The total strain energy stored in the spring assembly.
4. The stiffness of each spring.
5. The equivalent stiffness of a single spring that can be substituted in place of these springs.
A specimen of titanium alloy is tested in torsion and the shear stress–strain diagram is shown in Fig.a. Determine the shear modulus G, the proportional limit, and the ultimate shear stress. Also, determine the maximum distance d that the top of a block of this material, shown in Fig. b, could be displaced horizontally if the material behaves elastically when acted upon by a shear force V. What is the magnitude of V necessary to cause this displacement?
Stress (MPa)
500
400
Consider the brass alloy for which the stress-strain
behavior is shown in the Animated Figure 7.12. A
cylindrical specimen of this material 9.9mm (0.3898 in.)
in diameter and 98.8mm (3.890 in.) long is pulled in
tension with a force of 9780N(2199/b). If it is known
that this alloy has a value for Poisson's ratio of 0.35,
compute (a) the specimen elongation, (b) the reduction
in specimen diameter. Note: because the diameter
decreases, enter a minus sign in your answer.
Tensile strength
450 MPa (65,000 psi),
Strain =0
Stress = 0 MPA
Stress =0 psi
70
Strain = 0
Stress
0 MPA
60
Stress = 0 psi
103 psi
50
40
MPa
Yield strength
300
250 MPa (36,000 psi)
40
30
200
200
20
100
10
100
0
0
T
10
P
0.10
0.20
Strain
10.065
0
0.30
0.40
30
20
10
Stress (10 psi)
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
Ch. 2 - Prob. 2.1QCh. 2 - Prob. 2.2QCh. 2 - Prob. 2.3QCh. 2 - Prob. 2.4QCh. 2 - Prob. 2.5QCh. 2 - Prob. 2.6QCh. 2 - Prob. 2.7QCh. 2 - Prob. 2.8QCh. 2 - Prob. 2.9QCh. 2 - Prob. 2.10Q
Ch. 2 - Prob. 2.11QCh. 2 - Prob. 2.12QCh. 2 - Prob. 2.13QCh. 2 - Prob. 2.14QCh. 2 - Prob. 2.15QCh. 2 - Prob. 2.16QCh. 2 - Prob. 2.17QCh. 2 - Prob. 2.18QCh. 2 - Prob. 2.19QCh. 2 - Prob. 2.20QCh. 2 - Prob. 2.21QCh. 2 - Prob. 2.22QCh. 2 - Prob. 2.23QCh. 2 - Prob. 2.24QCh. 2 - Prob. 2.25QCh. 2 - Prob. 2.26QCh. 2 - Prob. 2.27QCh. 2 - Prob. 2.28QCh. 2 - Prob. 2.29QCh. 2 - Prob. 2.30QCh. 2 - Prob. 2.31QCh. 2 - Prob. 2.32QCh. 2 - Prob. 2.33QCh. 2 - Prob. 2.34QCh. 2 - Prob. 2.35QCh. 2 - Prob. 2.36QCh. 2 - Prob. 2.37QCh. 2 - Prob. 2.38QCh. 2 - Prob. 2.39QCh. 2 - Prob. 2.40QCh. 2 - Prob. 2.41QCh. 2 - Prob. 2.42QCh. 2 - Prob. 2.43QCh. 2 - Prob. 2.44QCh. 2 - Prob. 2.45QCh. 2 - Prob. 2.46QCh. 2 - Prob. 2.47QCh. 2 - Prob. 2.48QCh. 2 - Prob. 2.49PCh. 2 - Prob. 2.50PCh. 2 - Prob. 2.51PCh. 2 - Prob. 2.52PCh. 2 - Prob. 2.53PCh. 2 - Prob. 2.54PCh. 2 - Prob. 2.55PCh. 2 - Prob. 2.56PCh. 2 - Prob. 2.57PCh. 2 - Prob. 2.58PCh. 2 - Prob. 2.59PCh. 2 - Prob. 2.60PCh. 2 - Prob. 2.61PCh. 2 - Prob. 2.62PCh. 2 - Prob. 2.63PCh. 2 - Prob. 2.64PCh. 2 - Prob. 2.65PCh. 2 - Prob. 2.66PCh. 2 - Prob. 2.67PCh. 2 - Prob. 2.68PCh. 2 - Prob. 2.69PCh. 2 - Prob. 2.70PCh. 2 - Prob. 2.71PCh. 2 - Prob. 2.72PCh. 2 - Prob. 2.73PCh. 2 - Prob. 2.74PCh. 2 - Prob. 2.75PCh. 2 - Prob. 2.76PCh. 2 - Prob. 2.78PCh. 2 - Prob. 2.79PCh. 2 - Prob. 2.80PCh. 2 - Prob. 2.81PCh. 2 - Prob. 2.82PCh. 2 - Prob. 2.83PCh. 2 - Prob. 2.84PCh. 2 - Prob. 2.85PCh. 2 - Prob. 2.86PCh. 2 - Prob. 2.87PCh. 2 - Prob. 2.88PCh. 2 - Prob. 2.89PCh. 2 - Prob. 2.90PCh. 2 - Prob. 2.91PCh. 2 - Prob. 2.92PCh. 2 - Prob. 2.93PCh. 2 - Prob. 2.94PCh. 2 - Prob. 2.95PCh. 2 - Prob. 2.96PCh. 2 - Prob. 2.97PCh. 2 - Prob. 2.98PCh. 2 - Prob. 2.99PCh. 2 - Prob. 2.100PCh. 2 - Prob. 2.101P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm2 when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson’s ratio for both metallic rods. Justify your answer with reasons.arrow_forwardTensile test specimens are extracted from the "X" and "y" directions of a rolled sheet of metal. "x" is the rolling direction, "y" is transverse to the rolling direction, and "z" is in the thickness direction. Both specimens were pulled to a longitudinal strain = 0.15 strain. For the sample in the x-direction, the width strain was measured to be ew= -0.0923 at that instant. For the sample in the y-direction, the width strain was measured to be gw=-0.1000 at that instant. The yield strength of the x-direction specimen was 50 kpsi and the yield strength of the y-direction specimen was 52 kpsi. Determine the strain ratio for the x direction tensile test specimen. Determine the strain ratio for the y-direction tensile test specimen. Determine the expected yield strength in the z-direction. Give your answer in units of kpsi (just the number). If the sheet is plastically deformed in equal biaxial tension (a, = 0, to the point where & = 0.15, calculate the strain, 6, that would be expected.arrow_forwardThe data shown in the accompanying table are From a tensile test of high-strength steel. The test specimen has a diameter of 0.505 in. and a gage length of 2.00 in. (see figure for Prob. 1.5-3). At fracture, the elongation between the gage marks is 0.12 in. and the minimum diameter is 0.42 in. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (the slope of the initial part of thestress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 2.00 in., and percent reduction in area. TENSILE-TEST DATA FOR PROB. L.5-7 Laid (lb) Elongation (in) 1000 0.0002 2000 0.0006 6000 0.0019 10,000 0.0033 12,000 0.0039 12,900 0.0041 13,400 0.0047 13,600 0.0054 13,800 0.0063 14,000 0.0090 14,400 0.0102 15,200 0.0130 16,800 0.0230 18,400 0.0336 20,000 0.0507 22,400 0.1108 22,600 Fracturearrow_forward
- Scenario. Three specimen of D12 rebar was subjected to a Tensile Test. Using a steel density of 8000Kg/cu.m. With the following result specimen 1 specimen 2 M=0.895 kg M=0.89 kg L=98 cm L=99 cm Load at yield strength= 5000 kg Load at ultimate =8600 kg Gauge length after test=21.5 cm Load at yield strength= 5000 kg Load at ultimate =8600 kg Gauge length after test=21.6 cm specimen 3 M=0.897 kg L=100 cm Load at yield strength= 5010 kg Load at ultimate strength=8590 kg Gauge length after test=21.6 cm specimen Yield strength Yield strength Ultimate strength Ultimate strength STRAIN based on actual based on 12mm based on actual based on 12mm diameter (MPa) diameter (MPa) diameter (MPa) diameter (MPa) 1. 2. averagearrow_forwardA circular solid piece of rock is tested in a compression testing rig to examine its stress/strain behavior. The sample is 6 inches in diameter and 12 inches in length, with the compression load cell imposing a constant load of 10000 lbf equally at both the top and bottom of the rock sample. Assuming a measured reduction in length of 0.02 inches, find the compressive stress and strain of the rock.arrow_forwardA copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of diameter 12 mm and the indentation diameter 3.87 mm is measured using an optical magnifying lens with a ruler. Draw the Brinell Hardness Test setup neatly and determine the force applied on the specimen. Take Brinell Hardness Number for copper as 807. Calculate: 1-Surface Area of Indentation (in mm2) 2-Applied Force (in N)arrow_forward
- A steel rod 1 meter long with a cross-sectional area of 1200 mm² is stretched between two fixed points. The tensile force is 200 kN at 30°C. Using E = 200 GPa and a = 11.7μm/m°C, calculate (a) the temperature at which the stress in the bar will be 30 MPa; and (b) the temperature at which the stress will be zero.arrow_forwardA solid bar of length L = 4 m and diameter 100 mm is heated from 20 to 400 degrees celsius and restrained between two solid immovable walls. Young's modulus of the material is 95 GPa and the coefficient of thermal expansion is 23 x 10-6/°C. Calculate the thermal strain, e, in micro-strain correct to two decimal places. Calculate the thermal stress, o, in megapascals (MPa) correct to two decimal places. MPa. E: σ: micro-strain. Hence calculate the force exerted by the bar in meganewtons (MN) correct to two decimal places: F MN. Larrow_forwardThe strength coefficient and strain-hardening exponent of a certain test metal are 500MPa and 0.25 respectively. A cylindrical specimen of the metal with starting diameter = 58 mm is stretched. If the average flow stress on the part is 375 MPa determine the final diameter of the specimen.arrow_forward
- A steel rod, 16 mm in diameter and 5 m length, is connected to two grips at each end at a temperature of 150 °C. Find the pull exerted when the temperature falls to 40 °C, if the ends (i) do not yield and (ii) yield by 1 mm. Take coefficient of thermal expansion = per °C and N/mm 2arrow_forwardThe following stress-strain curve was prepared based on a tensile test of a specimen that had a circular cross-section. The gage diameter of the specimen was 0.25 inches and the gage length was 4 inches. The stress scale of the stress-strain diagram is given with the factor a = 10 ksi. Estimate: (a) The modulus of elasticity. (b) The ultimate strength. (c) The yield strength (0.2% offset). (d) The percent elongation at fracture. 2013 Michael Swanbom STRESS VS. STRAIN BY NC SA 7a bat Sat 2at at 0.05 STRAIN 0.01 0.04 0.06 0.08 0.02 0.03 0.07 0.09 STRESSarrow_forwardThe modulus of rigidity of a material is 63KN/mm2. A rod of diameter 40mm is subjected to an axial tensile force of 25kN and the change in its diameter is observed to be 0.002mm. Calculate v, E and K for the materialarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY